| dbo:abstract
|
- The five-cent coin was first issued as a silver coin of .800 fineness in 1866. It had a diameter of 15 mm, thickness of 0.80 mm, weighed 1.34 grams, and had a reeded edge. This coin was minted in silver until 1935, when its composition was changed to copper-nickel. It had an extensive mintage between 1866 and 1933, with some issued in 1932–33 with a plain edge. The coin was not minted in 1869–71, 1878, 1896, and 1906–1932. The following copper-nickel denomination was identical in all aspects except the composition and weight: it weighed 1.36 grams, 0.02 grams heavier than the previous coin. This was a one-year type as it was replaced with a pure nickel coin in 1937. This time, it had a diameter of 16.51 mm, was 1.73 mm thick, and weighed 2.59 grams. This was minted until 1941, with the last issue being scarce. Unlike the very rare 1941 Hong Kong one-cent coin these are available, although were never released to circulation because of the Japanese occupation. For a period of eight years the denomination was replaced by banknotes and the Japanese military yen. When reintroduced in 1949, it had the same specifications as the last issue, but was minted in nickel-brass. Until 1970 the issue had a reeded security edge; afterwards, it was only reeded. This coin was issued in 1949–50, 1958, 1960, 1963–65, 1967, 1971–72, and 1977–80, with a non-circulating coin issued in 1988. The 1964H issue is scarce. On 1 January 1989, the coin ceased to be used as currency. (en)
- La moneda de cinco centavos fue emitida por primera vez como una moneda de plata de .800 de finuras en 1866. Tenía un diámetro de 15 mm, grosor de 0.80 mm, pesaba 1.34 gramos, y tuvo un borde juncoso. Esta moneda fue acuñada en plata hasta 1935, cuándo su composición cambió a cuproníquel. Tuvo una extensa acuñación entre 1866 y 1933, y algunas se emitieron en 1932–33 con un borde plano. La moneda no fue acuñada en 1869–71, 1878, 1896, y 1906–1932. La siguiente denominación de cuproníquel era idéntica a su antecesora en todos los aspectos excepto la composición y peso: el peso era de1,36 gramos: 0,02 gramos más pesada que la anterior. Este fue un tipo de un año, cuando fue reemplazado con una moneda de níquel puro en 1937. Esta vez, tenía un diámetro de 16.51 mm, con un grosor de 1.73 mm, y un peso de 2.59 gramos. Esta fue acuñada hasta 1941, siendo el último número escaso. A diferencia de la muy rara moneda de de 1941, estos están disponibles, a pesar de que nunca se lanzaron a circulación debido a la ocupación japonesa. Por un período de ocho años la denominación fue reemplazada por billetes y el yen militar japonés. Cuándo se reintrodujo en 1949, tenga las mismas especificaciones como la última emisión, pero era acuñada en níquel-latón. Hasta 1970 la emisión tuvo un borde de seguridad juncado; después, sólo era juncado. Esta moneda fue emitida en 1949–50, 1958, 1960, 1963–65, 1967, 1971–72, y 1977–80, con una moneda no circulante emitida en 1988. La acuñación 1964H es escasa. El 1° de enero de 1989, la moneda cesó como moneda de uso vigente. (es)
- Гонкогнские пять центов (5¢) — разменная единица гонконгского доллара, равная пяти сотым. (ru)
- 香港五仙硬幣是一種過去流通的香港貨幣，面額為0.05港元，1989年1月1日停止流通。而斗零是廣東及香港市民（尤其是較年長者）習慣上對五仙的叫法。 (zh)
|
| rdfs:comment
|
- Гонкогнские пять центов (5¢) — разменная единица гонконгского доллара, равная пяти сотым. (ru)
- 香港五仙硬幣是一種過去流通的香港貨幣，面額為0.05港元，1989年1月1日停止流通。而斗零是廣東及香港市民（尤其是較年長者）習慣上對五仙的叫法。 (zh)
- The five-cent coin was first issued as a silver coin of .800 fineness in 1866. It had a diameter of 15 mm, thickness of 0.80 mm, weighed 1.34 grams, and had a reeded edge. This coin was minted in silver until 1935, when its composition was changed to copper-nickel. It had an extensive mintage between 1866 and 1933, with some issued in 1932–33 with a plain edge. The coin was not minted in 1869–71, 1878, 1896, and 1906–1932. The following copper-nickel denomination was identical in all aspects except the composition and weight: it weighed 1.36 grams, 0.02 grams heavier than the previous coin. This was a one-year type as it was replaced with a pure nickel coin in 1937. This time, it had a diameter of 16.51 mm, was 1.73 mm thick, and weighed 2.59 grams. This was minted until 1941, with the las (en)
- La moneda de cinco centavos fue emitida por primera vez como una moneda de plata de .800 de finuras en 1866. Tenía un diámetro de 15 mm, grosor de 0.80 mm, pesaba 1.34 gramos, y tuvo un borde juncoso. Esta moneda fue acuñada en plata hasta 1935, cuándo su composición cambió a cuproníquel. Tuvo una extensa acuñación entre 1866 y 1933, y algunas se emitieron en 1932–33 con un borde plano. La moneda no fue acuñada en 1869–71, 1878, 1896, y 1906–1932. La siguiente denominación de cuproníquel era idéntica a su antecesora en todos los aspectos excepto la composición y peso: el peso era de1,36 gramos: 0,02 gramos más pesada que la anterior. Este fue un tipo de un año, cuando fue reemplazado con una moneda de níquel puro en 1937. Esta vez, tenía un diámetro de 16.51 mm, con un grosor de 1.73 mm, y (es)
|