- Corrosion fatigue is fatigue in a corrosive environment. It is the mechanical degradation of a material under the joint action of corrosion and cyclic loading. Nearly all engineering structures experience some form of alternating stress, and are exposed to harmful environments during their service life. The environment plays a significant role in the fatigue of high-strength structural materials like steel, aluminum alloys and titanium alloys. Materials with high specific strength are being developed to meet the requirements of advancing technology. However, their usefulness depends to a large extent on the degree to which they resist corrosion fatigue. The effects of corrosive environments on the fatigue behavior of metals were studied as early as 1930. The phenomenon should not be confused with stress corrosion cracking, where corrosion (such as pitting) leads to the development of brittle cracks, growth and failure. The only requirement for corrosion fatigue is that the sample be under tensile stress. (en)
- Très comparable à la corrosion sous contrainte, le phénomène de fatigue-corrosion apparaît sous l'action conjuguée de l'environnement et d'une sollicitation mécanique cyclique. Il se manifeste par un abaissement de la résistance du matériau à la fatigue. Le plus souvent, et compte tenu des cinétiques de dissolution et de repassivation assez lentes comparées aux phénomènes mécaniques, ce type d'endommagement survient pour des pièces sollicitées à basse fréquence (fatigue oligocyclique), par exemple lors de cycles de chauffage-refroidissement de structures (fatigue thermique).Les mécanismes évoqués pour rendre compte de la fatigue-corrosion sont les mêmes que ceux présentés pour la corrosion sous contrainte, et les essais de laboratoire sont en général des essais de fatigue en présence du milieu considéré réalisés soit à amplitude de déformation (ε) constante, soit à amplitude de contrainte (σ) constante. (fr)
- 腐食疲労(ふしょくひろう、英: corrosion fatigue)とは、材料が腐食性環境下で繰返し応力を受けることで発生する疲労現象のことである。腐食作用と繰返し応力を同時に受けることで、それぞれが個々に作用した場合に比べて大きな材料損傷を発生させる。 (ja)
- Korrosionsutmattning är ett fenomen som beror på en kombination av korrosiv miljö och utmattning som kan ses som ett specialfall av spänningskorrosion. Utmattning innebär att ett material som utsätts för växlande laster utmattas och får kraftigt försämrade mekaniska egenskaper vilket ofta i slutänden leder till sprödbrott. Vid korrosionsutmattning sänks utmattningsgränsen eftersom den oftast transkristallina korrosionen försvagat materialet. (sv)
- Korozja zmęczeniowa jest wynikiem współdziałania korozji elektrochemicznej oraz zmiennych naprężeń spowodowanych powstaniem ostrych wżerów przechodzących w pęknięcia wypełnione produktami korozji. Uszkodzenia spowodowane korozją zmęczeniową są znacznie większe niż suma uszkodzeń wynikających z samego naprężenia zmiennego i korozji elektrochemicznej. (pl)
- Коррозионная усталость — разрушение материала под воздействием циклической динамической нагрузки и коррозионных сред. Почти все инженерные сооружения подвергаются воздействию внешних факторов во время их службы. Окружающая среда играет важную роль в усталости высокопрочных конструкционных материалов, таких как сталь, алюминиевые и титановые сплавы. В настоящее время разрабатываются материалы с высокой удельной прочностью, однако и их полезность, прежде всего, зависит именно от коррозионной усталости. Склонность материала к коррозионно-усталостному разрушению определяется его пределом выносливости, то есть способностью воспринимать нагрузки, вызывающие циклические напряжения в материале. Значительное влияние на величину коррозионной усталости оказывают свойства рабочей среды, параметры нагружения, количество примесей в основном материале, температура. (ru)
- 腐蚀疲劳（英文：Corrosion fatigue);材料疲劳伴随腐蚀加重而引起材料在它的一般疲劳极限之下就可能发生断裂。 为了满足先进技术的要求而制造高强度结构材料，如钢，铝合金和钛合金等。但它们的应用，在很大程度上要依赖它们的抗腐能力。这是很重要的。因此，早在1930年就有人开展腐蚀环境对金属疲劳的研究。 要注意区分腐蚀疲劳和应力腐蚀断裂的区别；腐蚀疲劳是因为腐蚀且受動態負載而扩展断裂；应力腐蚀断裂只要求材料受靜態負載。 (zh)
- Корозі́йна вто́ма (англ. corrosion fatigue) — руйнування металу під впливом періодичного динамічного навантаження (знакозмінних напружень) і корозійних середовищ. (uk)
|
| dbo:thumbnail
| |
| dbo:wikiPageID
| |
| dbo:wikiPageLength
|
- 9369 (xsd:nonNegativeInteger)
|
| dbo:wikiPageRevisionID
| |
| dbo:wikiPageWikiLink
| |
| dbp:wikiPageUsesTemplate
| |
| dcterms:subject
| |
| gold:hypernym
| |
| rdf:type
| |
| rdfs:comment
|
- 腐食疲労(ふしょくひろう、英: corrosion fatigue)とは、材料が腐食性環境下で繰返し応力を受けることで発生する疲労現象のことである。腐食作用と繰返し応力を同時に受けることで、それぞれが個々に作用した場合に比べて大きな材料損傷を発生させる。 (ja)
- Korrosionsutmattning är ett fenomen som beror på en kombination av korrosiv miljö och utmattning som kan ses som ett specialfall av spänningskorrosion. Utmattning innebär att ett material som utsätts för växlande laster utmattas och får kraftigt försämrade mekaniska egenskaper vilket ofta i slutänden leder till sprödbrott. Vid korrosionsutmattning sänks utmattningsgränsen eftersom den oftast transkristallina korrosionen försvagat materialet. (sv)
- Korozja zmęczeniowa jest wynikiem współdziałania korozji elektrochemicznej oraz zmiennych naprężeń spowodowanych powstaniem ostrych wżerów przechodzących w pęknięcia wypełnione produktami korozji. Uszkodzenia spowodowane korozją zmęczeniową są znacznie większe niż suma uszkodzeń wynikających z samego naprężenia zmiennego i korozji elektrochemicznej. (pl)
- 腐蚀疲劳（英文：Corrosion fatigue);材料疲劳伴随腐蚀加重而引起材料在它的一般疲劳极限之下就可能发生断裂。 为了满足先进技术的要求而制造高强度结构材料，如钢，铝合金和钛合金等。但它们的应用，在很大程度上要依赖它们的抗腐能力。这是很重要的。因此，早在1930年就有人开展腐蚀环境对金属疲劳的研究。 要注意区分腐蚀疲劳和应力腐蚀断裂的区别；腐蚀疲劳是因为腐蚀且受動態負載而扩展断裂；应力腐蚀断裂只要求材料受靜態負載。 (zh)
- Корозі́йна вто́ма (англ. corrosion fatigue) — руйнування металу під впливом періодичного динамічного навантаження (знакозмінних напружень) і корозійних середовищ. (uk)
- Corrosion fatigue is fatigue in a corrosive environment. It is the mechanical degradation of a material under the joint action of corrosion and cyclic loading. Nearly all engineering structures experience some form of alternating stress, and are exposed to harmful environments during their service life. The environment plays a significant role in the fatigue of high-strength structural materials like steel, aluminum alloys and titanium alloys. Materials with high specific strength are being developed to meet the requirements of advancing technology. However, their usefulness depends to a large extent on the degree to which they resist corrosion fatigue. (en)
- Très comparable à la corrosion sous contrainte, le phénomène de fatigue-corrosion apparaît sous l'action conjuguée de l'environnement et d'une sollicitation mécanique cyclique. Il se manifeste par un abaissement de la résistance du matériau à la fatigue. Le plus souvent, et compte tenu des cinétiques de dissolution et de repassivation assez lentes comparées aux phénomènes mécaniques, ce type d'endommagement survient pour des pièces sollicitées à basse fréquence (fatigue oligocyclique), par exemple lors de cycles de chauffage-refroidissement de structures (fatigue thermique).Les mécanismes évoqués pour rendre compte de la fatigue-corrosion sont les mêmes que ceux présentés pour la corrosion sous contrainte, et les essais de laboratoire sont en général des essais de fatigue en présence du mi (fr)
- Коррозионная усталость — разрушение материала под воздействием циклической динамической нагрузки и коррозионных сред. Почти все инженерные сооружения подвергаются воздействию внешних факторов во время их службы. Окружающая среда играет важную роль в усталости высокопрочных конструкционных материалов, таких как сталь, алюминиевые и титановые сплавы. В настоящее время разрабатываются материалы с высокой удельной прочностью, однако и их полезность, прежде всего, зависит именно от коррозионной усталости. (ru)
|
| rdfs:label
|
- Corrosion fatigue (en)
- Fatigue-corrosion (fr)
- 腐食疲労 (ja)
- Korozja zmęczeniowa (pl)
- Korrosionsutmattning (sv)
- Коррозионная усталость (ru)
- 腐蚀疲劳 (zh)
- Корозійна втома (uk)
|
| owl:sameAs
| |
| prov:wasDerivedFrom
| |
| foaf:depiction
| |
| foaf:isPrimaryTopicOf
| |
| is dbo:academicDiscipline
of | |
| is dbo:wikiPageRedirects
of | |
| is dbo:wikiPageWikiLink
of | |
| is foaf:primaryTopic
of | |