A secondary flux is a ceramic flux (such as calcium, barium, magnesium or zinc oxide) which does not act as a good flux (i.e., lower the melting point of the mixture) alone, but is effective when used in combination with other fluxes. They also tend to act as "anti-fluxes" at lower temperatures, and may produce matt or opaque glazes under those conditions. For example, calcium oxide is generally used with sodium or potassium and by itself has little fluxing effect at pyrometric cone 6 but does act as a flux at cone 8..When use calcium with lead it gives low melting temperature to glaz.

Property Value
dbo:abstract
  • A secondary flux is a ceramic flux (such as calcium, barium, magnesium or zinc oxide) which does not act as a good flux (i.e., lower the melting point of the mixture) alone, but is effective when used in combination with other fluxes. They also tend to act as "anti-fluxes" at lower temperatures, and may produce matt or opaque glazes under those conditions. For example, calcium oxide is generally used with sodium or potassium and by itself has little fluxing effect at pyrometric cone 6 but does act as a flux at cone 8..When use calcium with lead it gives low melting temperature to glaz. A primary flux is a metal ion such as sodium which acts as a flux at all temperatures. (en)
dbo:wikiPageID
  • 20798016 (xsd:integer)
dbo:wikiPageLength
  • 1061 (xsd:nonNegativeInteger)
dbo:wikiPageRevisionID
  • 1069874277 (xsd:integer)
dbo:wikiPageWikiLink
dbp:wikiPageUsesTemplate
dcterms:subject
gold:hypernym
rdf:type
rdfs:comment
  • A secondary flux is a ceramic flux (such as calcium, barium, magnesium or zinc oxide) which does not act as a good flux (i.e., lower the melting point of the mixture) alone, but is effective when used in combination with other fluxes. They also tend to act as "anti-fluxes" at lower temperatures, and may produce matt or opaque glazes under those conditions. For example, calcium oxide is generally used with sodium or potassium and by itself has little fluxing effect at pyrometric cone 6 but does act as a flux at cone 8..When use calcium with lead it gives low melting temperature to glaz. (en)
rdfs:label
  • Secondary flux (en)
owl:sameAs
prov:wasDerivedFrom
foaf:isPrimaryTopicOf
is dbo:wikiPageDisambiguates of
is dbo:wikiPageRedirects of
is dbo:wikiPageWikiLink of
is foaf:primaryTopic of
Powered by OpenLink Virtuoso    This material is Open Knowledge     W3C Semantic Web Technology     This material is Open Knowledge    Valid XHTML + RDFa
This content was extracted from Wikipedia and is licensed under the Creative Commons Attribution-ShareAlike 3.0 Unported License