Permendur is a cobalt-iron soft ferromagnetic alloy with equal parts of cobalt and iron which is notable for its high magnetic saturation level. Its saturation flux density of around 2.4 tesla is the highest of any commercially available metal. Coupled with its low coercivity and core losses, its high saturation and permeability makes Permendur useful as magnetic cores in transformers, electric generators and other electrical equipment. The advantage of high saturation in a magnetic core is that it can function at higher magnetic field strengths, so the core can be smaller and lighter for a given magnetic flux and power level. Permendur is used for magnetic cores and pole pieces in lightweight transformers and electric motors used in aircraft. The alloy was invented in 1929 by Gustav Elmen
| Attributes | Values |
|---|
| rdf:type
| |
| rdfs:label
| - Permendur (ca)
- パーメンジュール (ja)
- Permendur (en)
- Permendur (pl)
- Пермендюр (ru)
- Пермендюр (uk)
- 波門杜爾鐵鈷合金 (zh)
|
| rdfs:comment
| - Permendur és un aliatge magnètic formada per un 48-50% de cobalt, Co, un 48-50% de ferro, Fe i un 2% de vanadi, V. Té una alta permeabilitat magnètica amb una temperatura de Curie de 980 °С. Fou preparada al voltant de l'any 1920 als Estats Units d'Amèrica. Les seves aplicacions són generadors elèctrics, pols d'electroimants, coixinets magnètics i dispositius d'alt flux magnètic i, en general, per a tots aquells aparells elèctrics que requereixin un elevat flux magnètic. (ca)
- パーメンジュール (permendur) は、鉄とコバルトを1対1の割合で混ぜた合金である。 実用化された軟磁性材料の中で最大の飽和磁束密度を持つことから、電磁石の鉄芯や励磁型のスピーカー、電子顕微鏡の磁界レンズ、ドットプリンターヘッド、人工心臓用平板状リニアパルスモータ等に用いられる。 730 ℃付近からの冷却速度が遅いと、規則化によって著しく脆くなる。 組成例（重量%）は、Fe-49Co-2V , Fe-20Co-V (ja)
- Пермендю́р (англ. permendur: permeability — «проницаемость»; durable — «прочный») — сплав железа (47-50 %) с кобальтом (48-50 %), с небольшой добавкой ванадия (1.5-2 %). Сплав разработан в США в 1920-х годах. Обладает свойством насыщения магнитной проницаемости при очень высоких значениях индукции магнитного поля (2-2,4 Тл). Ограниченно применяется в изготовлении наконечников электромагнитов и других устройствах. В России пермендюром называют сплав марки К49Ф2. (ru)
- 波門杜爾鐵鈷合金（Permendur）是鐵鈷的軟磁合金，其中鐵和鈷的比例相同，1920年在美國發明。其俄語名稱為пермендюр (49К2ФА) 。 標準的波門杜爾鐵鈷合金稱為Fe-Co 50/50或50Fe-50Co，其中最多會含有1%的碳。但1932年有一種已註冊的合金，稱為Vanadium Permendur及Permendur 2V，最近由Goodfellow公司提供，名稱為Permendur 49 （其成份都是49Fe-49Co-2V），含有2%的釩以提昇機械性質及加工性。Carpenter科技有生產類似的合金，稱為Supermendur及V-Permendur，最近更名為Hiperco 50，最新的成份中，鐵、鈷、釩的比例不變，但加入了痕量的鈮、矽及錳以提昇可鍛性及冷加工的可加工性。Vacuumschmelze生產了48%...50% 鈷合金，名稱為VACOFLUX及VACODUR。 50Fe-50Co及49Fe-49Co-2V有高磁導率、磁損失小的特性，在商用的軟磁合金中，其在磁飽和點有最大的磁通密度高（若感應飽和，約23000-24000高斯）。其磁轉態溫度為980 °С。 (zh)
- Permendur is a cobalt-iron soft ferromagnetic alloy with equal parts of cobalt and iron which is notable for its high magnetic saturation level. Its saturation flux density of around 2.4 tesla is the highest of any commercially available metal. Coupled with its low coercivity and core losses, its high saturation and permeability makes Permendur useful as magnetic cores in transformers, electric generators and other electrical equipment. The advantage of high saturation in a magnetic core is that it can function at higher magnetic field strengths, so the core can be smaller and lighter for a given magnetic flux and power level. Permendur is used for magnetic cores and pole pieces in lightweight transformers and electric motors used in aircraft. The alloy was invented in 1929 by Gustav Elmen (en)
- Permendur – stop żelaza z kobaltem i niewielkimi dodatkami wanadu (do 2%), tantalu i niobu. Permendur charakteryzuje się bardzo wysoką indukcją nasycenia – do 2,43 T. Jest to obecnie najwyższa znana wartość indukcji nasycenia dla materiałów magnetycznie miękkich. Rozróżnia się dwa podstawowe składy chemiczne permenduru: Siła F mechanicznego oddziaływania pomiędzy namagnesowanymi powierzchniami jest wprost proporcjonalna do kwadratu indukcji magnetycznej B: (pl)
- Пермендю́р (англ. permendur: permeability — «проникність»; durable — «міцний») — прецизійний магніто-м'який сплав заліза (47-50%) з кобальтом (48-50%), та малим доданком ванадію (1.5-2%). Здешевлений варіант сплаву містить близько 24% кобальту. Сплав створено в США в 1920-х роках. Характеризується властивістю насичення магнітної проникності за дуже високих значень індукції магнітного поля (2-2.4 Тл). За ГОСТ 10994-74 сплави маркуються як 49К2Ф, 49К2Ф2, 49КФ (аналоги Permendur-49), 27КХ (аналог Permendur-24). (uk)
|
| foaf:depiction
| |
| dcterms:subject
| |
| Wikipage page ID
| |
| Wikipage revision ID
| |
| Link from a Wikipage to another Wikipage
| |
| sameAs
| |
| dbp:wikiPageUsesTemplate
| |
| thumbnail
| |
| has abstract
| - Permendur és un aliatge magnètic formada per un 48-50% de cobalt, Co, un 48-50% de ferro, Fe i un 2% de vanadi, V. Té una alta permeabilitat magnètica amb una temperatura de Curie de 980 °С. Fou preparada al voltant de l'any 1920 als Estats Units d'Amèrica. Les seves aplicacions són generadors elèctrics, pols d'electroimants, coixinets magnètics i dispositius d'alt flux magnètic i, en general, per a tots aquells aparells elèctrics que requereixin un elevat flux magnètic. (ca)
- Permendur is a cobalt-iron soft ferromagnetic alloy with equal parts of cobalt and iron which is notable for its high magnetic saturation level. Its saturation flux density of around 2.4 tesla is the highest of any commercially available metal. Coupled with its low coercivity and core losses, its high saturation and permeability makes Permendur useful as magnetic cores in transformers, electric generators and other electrical equipment. The advantage of high saturation in a magnetic core is that it can function at higher magnetic field strengths, so the core can be smaller and lighter for a given magnetic flux and power level. Permendur is used for magnetic cores and pole pieces in lightweight transformers and electric motors used in aircraft. The alloy was invented in 1929 by Gustav Elmen at Bell Telephone Laboratories. Various formulations are sold under different trade names. Cobalt-iron alloys like permendur have very high Curie temperatures so they can function magnetically at high temperatures at which other ferromagnetic materials lose their magnetic properties. They are harder and less ductile than many other iron alloys and so are harder to fabricate, but have superior mechanical strength. Most permendur alloys require heat treatment after fabrication to attain the best magnetic properties. The most important alloys are
* Permendur 2V (Vanadium Permendur, Permendur 49): Invented by White and Wahl in 1932, it is approximately 49% cobalt, 49% iron and 2% vanadium. The vanadium improves ductility and workability.
* Supermendur (Hiperco 50): Invented by Gould and Wenny in 1957, it has similar composition to Permendur 49 but is grain-oriented so it has a square hysteresis loop and much lower core losses, for better performance in transformers. Current formulations include trace amounts of niobium, silicon and manganese to improve cold-forming properties. The coercivity can be controlled by varying the vanadium concentration. Equiatomic cobalt-iron alloys with more vanadium than permendur, 2-5%, are called Remendur. This is a medium-coercivity magnet material which bridges the gap between Permendur and Vicalloy cobalt-iron magnets with 8-15% vanadium. (en)
- パーメンジュール (permendur) は、鉄とコバルトを1対1の割合で混ぜた合金である。 実用化された軟磁性材料の中で最大の飽和磁束密度を持つことから、電磁石の鉄芯や励磁型のスピーカー、電子顕微鏡の磁界レンズ、ドットプリンターヘッド、人工心臓用平板状リニアパルスモータ等に用いられる。 730 ℃付近からの冷却速度が遅いと、規則化によって著しく脆くなる。 組成例（重量%）は、Fe-49Co-2V , Fe-20Co-V (ja)
- Permendur – stop żelaza z kobaltem i niewielkimi dodatkami wanadu (do 2%), tantalu i niobu. Permendur charakteryzuje się bardzo wysoką indukcją nasycenia – do 2,43 T. Jest to obecnie najwyższa znana wartość indukcji nasycenia dla materiałów magnetycznie miękkich. Rozróżnia się dwa podstawowe składy chemiczne permenduru:
* Permendur 49 z wysoką zawartością kobaltu (około 49%), który charakteryzuje się wyższą indukcją nasycenia, ale również zwiększonym kosztem stopu z uwagi na relatywnie drogi kobalt.
* Permendur 24 ze zmniejszoną zawartością kobaltu (około 24%), który jest tańszy, ale również jego indukcja nasycenia jest nieco mniejsza. Siła F mechanicznego oddziaływania pomiędzy namagnesowanymi powierzchniami jest wprost proporcjonalna do kwadratu indukcji magnetycznej B: Dlatego też permendur stosowany jest wszędzie tam, gdzie zachodzi konieczność uzyskania maksymalnej siły lub momentu siły i w konsekwencji sprawności urządzenia – na przykład w maszynach elektrycznych używanych w samolotach lub satelitach kosmicznych. (pl)
- Пермендю́р (англ. permendur: permeability — «проницаемость»; durable — «прочный») — сплав железа (47-50 %) с кобальтом (48-50 %), с небольшой добавкой ванадия (1.5-2 %). Сплав разработан в США в 1920-х годах. Обладает свойством насыщения магнитной проницаемости при очень высоких значениях индукции магнитного поля (2-2,4 Тл). Ограниченно применяется в изготовлении наконечников электромагнитов и других устройствах. В России пермендюром называют сплав марки К49Ф2. (ru)
- Пермендю́р (англ. permendur: permeability — «проникність»; durable — «міцний») — прецизійний магніто-м'який сплав заліза (47-50%) з кобальтом (48-50%), та малим доданком ванадію (1.5-2%). Здешевлений варіант сплаву містить близько 24% кобальту. Сплав створено в США в 1920-х роках. Характеризується властивістю насичення магнітної проникності за дуже високих значень індукції магнітного поля (2-2.4 Тл). За ГОСТ 10994-74 сплави маркуються як 49К2Ф, 49К2Ф2, 49КФ (аналоги Permendur-49), 27КХ (аналог Permendur-24). За значеннями магнітної проникності в полях, напруженість яких >4 А/см і за точкою Кюрі, яка становить 950-980 °C, пермендюр значно перевищує електротехнічну сталь та залізо. Застосовується для виготовлення полюсних кінців електромагнітів, роторних пластин малогабаритних електродвигунів та інших приладів, де необхідно сконцентрувати в малому просторі потужний потік різних силових ліній. Оскільки матеріал не має дефектів, що підвищують опір руху меж магнітних доменів, то в ньому відсутня кристалографічна анізотропія. (uk)
- 波門杜爾鐵鈷合金（Permendur）是鐵鈷的軟磁合金，其中鐵和鈷的比例相同，1920年在美國發明。其俄語名稱為пермендюр (49К2ФА) 。 標準的波門杜爾鐵鈷合金稱為Fe-Co 50/50或50Fe-50Co，其中最多會含有1%的碳。但1932年有一種已註冊的合金，稱為Vanadium Permendur及Permendur 2V，最近由Goodfellow公司提供，名稱為Permendur 49 （其成份都是49Fe-49Co-2V），含有2%的釩以提昇機械性質及加工性。Carpenter科技有生產類似的合金，稱為Supermendur及V-Permendur，最近更名為Hiperco 50，最新的成份中，鐵、鈷、釩的比例不變，但加入了痕量的鈮、矽及錳以提昇可鍛性及冷加工的可加工性。Vacuumschmelze生產了48%...50% 鈷合金，名稱為VACOFLUX及VACODUR。 50Fe-50Co及49Fe-49Co-2V有高磁導率、磁損失小的特性，在商用的軟磁合金中，其在磁飽和點有最大的磁通密度高（若感應飽和，約23000-24000高斯）。其磁轉態溫度為980 °С。 (zh)
|
| gold:hypernym
| |
| prov:wasDerivedFrom
| |
| page length (characters) of wiki page
| |
| foaf:isPrimaryTopicOf
| |
| is Link from a Wikipage to another Wikipage
of | |
| is foaf:primaryTopic
of | |
![[RDF Data]](/fct/images/sw-rdf-blue.png)
![[cxml]](/fct/images/cxml_doc.png)
![[csv]](/fct/images/csv_doc.png)
![[text]](/fct/images/ntriples_doc.png)
![[turtle]](/fct/images/n3turtle_doc.png)
![[ld+json]](/fct/images/jsonld_doc.png)
![[rdf+json]](/fct/images/json_doc.png)
![[rdf+xml]](/fct/images/xml_doc.png)
![[atom+xml]](/fct/images/atom_doc.png)
![[html]](/fct/images/html_doc.png)