The Edison–Lalande cell was a type of alkaline primary battery developed by Thomas Edison from an earlier design by and . It consisted of plates of copper oxide and zinc in a solution of potassium hydroxide. The cell voltage was low (about 0.75 volts) but the internal resistance was also low so these cells were capable of delivering large currents. The cell could be replenished with fresh zinc and copper oxide plates and KOH solution for reuse.
Attributes | Values |
---|
rdf:type
| |
rdfs:label
| - Edison–Lalande cell (en)
- Edison-Lalande-Element (de)
- Celda de Edison-Lalande (es)
- Pilha de Edison-Lalande (pt)
- Медно-окисный гальванический элемент (ru)
|
rdfs:comment
| - The Edison–Lalande cell was a type of alkaline primary battery developed by Thomas Edison from an earlier design by and . It consisted of plates of copper oxide and zinc in a solution of potassium hydroxide. The cell voltage was low (about 0.75 volts) but the internal resistance was also low so these cells were capable of delivering large currents. The cell could be replenished with fresh zinc and copper oxide plates and KOH solution for reuse. (en)
- La célula de Edison-Lalande era un tipo de pila primaria alcalina desarrollada por Thomas Edison de un diseño anterior por y . Se trataba de placas de óxido de cobre y zinc en una solución de hidróxido de potasio. El voltaje de la célula fue bajo (aproximadamente 0,75 voltios), pero la resistencia interna también fue baja, por lo que estas células eran capaces de suministrar grandes corrientes. (es)
- Ме́дно-о́кисный гальвани́ческий элеме́нт — химический источник тока, в котором анодом является цинк (реже олово), электролитом — гидроксид калия, катодом — оксид меди[уточнить] (иногда с добавлением оксида бария для увеличения ёмкости или оксида висмута[уточнить]). (ru)
- A Pilha Edison-Lalande é um tipo de pilha primária alcalina desenvolvido por Thomas Edison a partir de um desenho anterior criado por Felix Lalande e Georges Chaperon. Consiste de placas de óxido de cobre e de zinco numa solução de hidróxido de potássio. A tensão da célula é baixa (cerca de 0,75 volts) e sua resistência interna também é baixa. Porém elas são capazes de fornecer uma corrente elevada. (pt)
- Das Edison-Lalande-Element ist eine historische Bauform einer elektrisch nicht wiederaufladbaren Primärzelle. Sie wurde von Thomas Alva Edison, nach Vorarbeiten von und , gegen Ende des 19. Jahrhunderts entwickelt. Die ursprüngliche Zelle von Lalande und Chaperon bestand aus einer Elektrode aus Zink und pulverförmigen Kupferoxid und einem flüssigen Elektrolyt aus im Wasser gelösten Kaliumhydroxid. Edison verbesserte konstruktiv den Aufbau, indem er das pulverförmige Kupferoxid durch Pressstücke aus Kupferoxid ersetzte. (de)
|
foaf:name
| |
foaf:depiction
| |
dcterms:subject
| |
Wikipage page ID
| |
Wikipage revision ID
| |
Link from a Wikipage to another Wikipage
| |
sameAs
| |
dbp:wikiPageUsesTemplate
| |
thumbnail
| |
caption
| |
has abstract
| - The Edison–Lalande cell was a type of alkaline primary battery developed by Thomas Edison from an earlier design by and . It consisted of plates of copper oxide and zinc in a solution of potassium hydroxide. The cell voltage was low (about 0.75 volts) but the internal resistance was also low so these cells were capable of delivering large currents. The cell could be replenished with fresh zinc and copper oxide plates and KOH solution for reuse. (en)
- Das Edison-Lalande-Element ist eine historische Bauform einer elektrisch nicht wiederaufladbaren Primärzelle. Sie wurde von Thomas Alva Edison, nach Vorarbeiten von und , gegen Ende des 19. Jahrhunderts entwickelt. Die ursprüngliche Zelle von Lalande und Chaperon bestand aus einer Elektrode aus Zink und pulverförmigen Kupferoxid und einem flüssigen Elektrolyt aus im Wasser gelösten Kaliumhydroxid. Edison verbesserte konstruktiv den Aufbau, indem er das pulverförmige Kupferoxid durch Pressstücke aus Kupferoxid ersetzte. Die Zellspannung beträgt bei dem Edison-Lalande-Element 0,75 V, was gegenüber anderen zeitgenössischen galvanischen Elementen wie dem Gravity-Daniell-Element mit höheren Zellspannungen einen Nachteil darstellte, dafür ist der Innenwiderstand der Zelle kleiner und erlaubt höhere Entladeströme. (de)
- La célula de Edison-Lalande era un tipo de pila primaria alcalina desarrollada por Thomas Edison de un diseño anterior por y . Se trataba de placas de óxido de cobre y zinc en una solución de hidróxido de potasio. El voltaje de la célula fue bajo (aproximadamente 0,75 voltios), pero la resistencia interna también fue baja, por lo que estas células eran capaces de suministrar grandes corrientes. (es)
- Ме́дно-о́кисный гальвани́ческий элеме́нт — химический источник тока, в котором анодом является цинк (реже олово), электролитом — гидроксид калия, катодом — оксид меди[уточнить] (иногда с добавлением оксида бария для увеличения ёмкости или оксида висмута[уточнить]). (ru)
- A Pilha Edison-Lalande é um tipo de pilha primária alcalina desenvolvido por Thomas Edison a partir de um desenho anterior criado por Felix Lalande e Georges Chaperon. Consiste de placas de óxido de cobre e de zinco numa solução de hidróxido de potássio. A tensão da célula é baixa (cerca de 0,75 volts) e sua resistência interna também é baixa. Porém elas são capazes de fornecer uma corrente elevada. (pt)
|
gold:hypernym
| |
prov:wasDerivedFrom
| |
page length (characters) of wiki page
| |
foaf:isPrimaryTopicOf
| |
is Link from a Wikipage to another Wikipage
of | |
is Wikipage redirect
of | |
is Wikipage disambiguates
of | |
is known for
of | |
is known for
of | |
is foaf:primaryTopic
of | |