Cast iron is a group of iron-carbon alloys with a carbon content more than 2%. Its usefulness derives from its relatively low melting temperature. The alloy constituents affect its colour when fractured: white cast iron has carbide impurities which allow cracks to pass straight through, grey cast iron has graphite flakes which deflect a passing crack and initiate countless new cracks as the material breaks, and ductile cast iron has spherical graphite "nodules" which stop the crack from further progressing.

AttributesValues
rdf:type
rdfs:label
  • Cast iron
  • حديد زهر
  • Ferro colat
  • Litina
  • Gusseisen
  • Gisfero
  • Fundición de hierro
  • Fonte (métallurgie)
  • Iarann teilgthe
  • Besi tuang
  • Ghisa
  • 鋳鉄
  • 주철
  • Gietijzer
  • Żeliwo
  • Ferro fundido
  • Чугун
  • Gjutjärn
  • Чавун
  • 铸铁
rdfs:comment
  • Litina je slitina železa s uhlíkem. Uhlíku obsahuje více než 2,11 % podle binárního diagramu železo-uhlík. Při obsazích uhlíku nižších než 2,11 % se hovoří o ocelích. Má vysokou odolnost vůči tlaku a teplotě a zároveň nízkou pružnost. Litiny, u kterých je uhlík vyloučen ve formě grafitu, jsou tzv. litiny samomazné.Výrazem litina se označují také výrobky z litého železa, často umělecky zpracované, např. reliéfní desky kamen a krbů, náhrobky, kříže, dekorativní předměty i šperky.
  • Gusseisen ist ein Eisenwerkstoff mit hohem Kohlenstoffgehalt (Massenanteil über 2 %), der diesen Werkstoff von Stahl unterscheidet. Gusseisen weist eine gute Gießbarkeit auf (geringer Schmelzpunkt, dünnflüssige Schmelze, …), lässt sich aber nicht durch Schmieden bearbeiten, da es hart und spröde ist. Stahl dagegen lässt sich relativ schlecht gießen, aber sehr gut schmieden. Die Zerspanbarkeit von Gusseisen hängt von der genauen Sorte ab; bei Gusseisen mit Lamellengraphit – der häufigsten Sorte – ist sie gut. Seine Festigkeit ist geringer als die von Stahlguss, die Dämpfung aber höher.
  • Gisfero, aŭ pli simple giso, estas grupo de feraj alojoj kun relative granda enteno da karbo (> 2 %) kaj silicio (> 1,5 %) kaj aliaj materialoj kiel mangano, kromo aŭ nikelo. Oni diferencigas inter la griza gisfero, en kiu la karbo aperas en formo de grafito, kaj la blanka gisfero, en kiu la karbo aperas en formo de . Gisfero havas la denson je ĉirkaŭ 7 200 kg/m³, kiu estas malpli granda ol tiu de la ŝtalo kaj pura fero (7 850 kg/m³). La materialo havas la fandopunkton je 1150 °C.
  • Príomhtháirge an fhoirnéis soinneáin, iarann le timpeall 4% carbóin (garbhiarann). Leáphointe réasúnta íseal aige, agus glacann sé cruth an mhúnla go réasúnta nuair a reonn sé. Mar sin, is maith é chun teilgthe, ach is gá é a íonú nó a mhionathrú chun earraí a dhéanamh as. Is féidir é a mheaisíniú go maith freisin, ach tá míbhuntáistí suntasacha aige, go bhfuil sé briosc agus neart inteannta íseal aige. Is féidir é a chóireáil chun foirm na gcuimsiúcháin carbóin a mhionathrú agus iarann sféaróideach teilgthe le hairíonna feabhsaithe a tháirgeadh. San am atá thart d'úsáidtí iarann teilgthe mar ábhar tógála mar go bhfuil neart comhbhrúite an-ard aige.
  • La fonte, en métallurgie, est un alliage de fer et de carbone dont la teneur est supérieure à 2%. Le carbone, qui est en sursaturation dans les fontes, peut précipiter sous forme de graphite ou de cémentite Fe3C. Elles se distinguent par rapport aux autres alliages de par leur excellente coulabilité. Plusieurs classifications des fontes existent, mais la plus utilisée, basée sur le faciès de rupture d'un témoin, définit deux catégories : les fontes blanches, à cassure blanche, constituées de fer et de cémentite et les fontes grises, à cassure grise, constituées de fer et de graphite.
  • 鋳鉄(ちゅうてつ、cast iron)とは、 1. * 通俗的には、鉄を使った鋳物製品全般、またそこに用いられている鉄のこと。 2. * 学術・産業上は、炭素 Cを2.14 - 6.67%、ケイ素 Siを約1 - 3%の範囲で含む鉄 Feのの意味。 以下、後者について解説する。
  • Gietijzer is een in vormen gegoten legering van ijzer, koolstof (2,5%-6,67%), mangaan en silicium. Het wordt vervaardigd door omsmelting van ruw ijzer samen met cokes (kooks) en kalk in een koepeloven, inductieoven of trommeloven. Vanwege de ruwheid van het oppervlak is het uiterlijk van een gietijzeren voorwerp duidelijk als zodanig te herkennen.
  • O ferro fundido é uma liga de ferro em mistura eutética com elementos à base de carbono e silício. Forma uma liga metálica de ferro, carbono (a partir de 2% a 7%), silício (entre 1 e 4%), podendo conter outros elementos químicos. Sua diferença para o aço é que este também é uma liga metálica formada essencialmente por ferro e carbono, mas com percentagens entre 0,002 e 2,15%. Os ferros fundidos dividem-se em três tipos principais: branco, cinzento e nodular.
  • Gjutjärn är järn med en kolhalt mellan ungefär 2,12 och 4 procent. Beroende på kemisk sammansättning och svalningshastighet så fås olika slags gjutjärn.
  • 铸铁(英語:Cast iron)是指含碳量在2%~6.67%的铸造铁碳合金的总称,通常由生铁、废钢、铁合金等以不同比例配合通过熔炼而成。 主要元素除铁、碳以外还有硅、锰和少量的磷与硫等元素,是将生铁(有时有炼钢生铁)重新回炉熔化,并加进铁合金、废钢、回炉铁调整成分而得到的。
  • الحديد الزهر يسمى أيضًا الحديد السبك[محل شك] أو الحديد الصب وهو الحديد الناتج من الأفران العالية وتبلغ كثافته 7.86 جم/سم3، و درجة انصهاره ما بين 1,275 إلى 1,505 درجة مئوية. وهو سهل الكسر و لا يقبل التشكيل. ترجع هشاشة حديد الزهر إلى النسبة العالية من الكربون فيه، فهي تكون أعلى من 06و2%. ويحتوي حديد الزهر على نسبة كربون تفوق حد ذوبانه في طور الأوستنيت عند درجة حرارة اليوتكتي فينفصل الكربون في صورة قشور أو شبه كريات (حديد زهر رمادي) أو قد يكوّن سمنتيتاً (حديد زهر أبيض).
  • Una fosa o ferro colat és un aliatge de ferro amb més d'un 2% de carboni. Les foses presenten una elevada colabilitat, cosa que fa que s'utilitzin molt en peces fabricades per fusió i emmotllament (p. ex. blocs de motor, cossos de vàlvules...) La fosa metal·lúrgica deriva del lingot d'alt forn, i normalment es refereix al ferro gris, també identifica un gran grup d'aliatges ferrosos que solidifiquen eutècticament. El color de la seva superfície fracturada es pot usar per identificar els seus aliatges.
  • Cast iron is a group of iron-carbon alloys with a carbon content more than 2%. Its usefulness derives from its relatively low melting temperature. The alloy constituents affect its colour when fractured: white cast iron has carbide impurities which allow cracks to pass straight through, grey cast iron has graphite flakes which deflect a passing crack and initiate countless new cracks as the material breaks, and ductile cast iron has spherical graphite "nodules" which stop the crack from further progressing.
  • Las fundiciones son aleaciones hierro-carbono donde el contenido de carbono varía entre 2,14% y 6,67% (aunque estos porcentajes no son completamente rígidos).Comúnmente las más usadas están entre los valores de 2,5% y 4,5%, ya que las de mayor contenido de carbono carecen de valor práctico en la industria. Además de hierro y carbono, lleva otros elementos de aleación como silicio, manganeso, fósforo, azufre y oxígeno. Seguirán el (Fe-C) (o su porción Fe-Fe3C) o metaestable dependiendo de distintos factores, principalmente de si se produce o no la . Se dividen en dos tipos:
  • Besi tuang atau besi cor (bahasa Inggris: cast iron) adalah paduan besi-karbon dengan kandungan karbon lebih dari 2%. Paduan besi dengan kandungan karbon kurang dari 2% disebut sebagai baja. Unsur paduan utama yang membentuk karakter besi tuang adalah karbon (C) antara 3-3,5% dan silikon (Si) antara 1,8-2,4%. Perbedaan kadar C dan Si menyebabkan titik lebur besi tuang lebih rendah dari baja, yakni sekitar 1.150 sampai 1.200° C. Unsur paduan yang terkandung didalamnya mempengaruhi warna patahannya; besi tuang putih mengandung unsur karbida sedangkan besi tuang kelabu mengandung serpihan grafit.
  • La ghisa (detta anche fino all'Ottocento ferraccio per la minore qualità e la peggiore lavorabilità rispetto all'acciaio dolce) è una lega ferrosa costituita principalmente da ferro e carbonio con tenore di carbonio relativamente alto (2,06% < C < 6,67% che è il limite di saturazione) ottenuta per riduzione o trattamento a caldo dei minerali di ferro. Le ghise si classificano come ipoeutettiche, eutettiche o ipereutettiche se il tenore di carbonio è rispettivamente minore di 4,3%, uguale a 4,3% o maggiore di 4,3%. Le leghe ferrose con tenore di carbonio 0,08% < C < 2,06% sono gli acciai.
  • 주철(鑄鐵, Cast iron)은 1.7% 이상의 탄소를 함유하는 철의 합금이다. 보통 탄소량은 2.06 ~ 6.7%로 나타나 있으나 흔히 사용되는 것은 3 ~ 4%이다. 탄소가 많아서 단단하고 부서지기가 쉬우므로 압연·단조 등의 가공은 할 수 없으나, 강에 비해서 융점이 낮아 쉽게 용해되기 때문에 주물로 쓰기에는 편리하다. 주철 제품은 강도가 높고 강에 비해 녹이 덜 슬며 가격도 싸기 때문에 기계 부품에서 취사용구에 이르기까지 용도가 넓고 또 많이 쓰이고 있다. 주철의 탄소는 (영어: cementite)(Fe3C)의 형태로 존재하는 경우와 단독의 탄소가 흑연의 형태로 존재하는 경우의 두 가지가 있으며, 또한 주철로서의 성질도 다르다. 탄소가 세멘타이트의 형태로 되느냐, 흑연의 형태로 되느냐 하는 것은 주철 속의 탄소와 규소의 양 및 주조할 때의 냉각 속도에 관계된다. 탄소나 규소가 적고 급랭되면 세멘타이트로 된다. 세멘타이트는 굳은 화합물이므로, 세멘타이트를 많이 함유하는 주철은 단단하고 내마모성(耐磨耗性)은 우수하지만 부서지기가 쉽다. 이와 같은 주철의 단면은 조직이 치밀하고 백색으로 빛나기 때문에 백주철이라고 한다.
  • Żeliwo – wysokowęglowy stop żelaza z węglem, zazwyczaj także z krzemem, manganem, fosforem, siarką i innymi składnikami. Zawiera od 2,11 do 6,67% węgla w postaci cementytu lub grafitu. Występowanie konkretnej fazy węgla zależy od szybkości chłodzenia i składu chemicznego stopu. Chłodzenie powolne sprzyja wydzielaniu się grafitu. Także i dodatki stopowe odgrywają tu pewną rolę. Według obowiązującej normy żeliwo definiuje się jako tworzywo, którego głównym składnikiem jest żelazo i w którym zawartość węgla przekracza 2% (obecność dużych zawartości składników może zmienić podaną zawartość węgla).
  • Чугу́н — сплав железа с углеродом (и другими элементами), в котором содержание углерода не менее 2,14 % (точка предельной растворимости углерода в аустените на диаграмме состояний), а сплавы с содержанием углерода менее 2,14 % называются сталью. Углерод придаёт сплавам железа твёрдость, снижая пластичность и вязкость. Углерод в чугуне может содержаться в виде цементита и графита. В зависимости от формы графита и количества цементита, выделяют белый, серый, ковкий и высокопрочный чугуны. Чугуны содержат постоянные примеси (Si, Mn, S, P), а в некоторых случаях также легирующие элементы (Cr, Ni, V, Al и другие). Как правило, чугун хрупок.
  • Чаву́н — сплав заліза з вуглецем (понад 2 % вуглецю за масою) та іншими елементами, який характеризується наявністю евтектичного перетворення: нестабільного (цементитного) або стабільного (графітного). Чисте залізо має обмежене застосування. В техніці зазвичай використовують сплави заліза з вуглецем, які поділяють на сталі і чавуни. Сталі містять до 2 % вуглецю, а чавуни — від 2,14 до 4 % вуглецю і навіть більше. Слово «чавун» походить з тюркських мов, до яких воно потрапило, імовірно, з китайської мови.
rdfs:seeAlso
foaf:depiction
  • External Image
foaf:isPrimaryTopicOf
thumbnail
dct:subject
Wikipage page ID
Wikipage revision ID
Link from a Wikipage to another Wikipage
Faceted Search & Find service v1.17_git51 as of Sep 16 2020


Alternative Linked Data Documents: PivotViewer | iSPARQL | ODE     Content Formats:       RDF       ODATA       Microdata      About   
This material is Open Knowledge   W3C Semantic Web Technology [RDF Data] Valid XHTML + RDFa
OpenLink Virtuoso version 08.03.3319 as of Dec 29 2020, on Linux (x86_64-centos_6-linux-glibc2.12), Single-Server Edition (61 GB total memory)
Data on this page belongs to its respective rights holders.
Virtuoso Faceted Browser Copyright © 2009-2021 OpenLink Software